首页 理论教育 钎焊接头强度测试:强度评估与分析

钎焊接头强度测试:强度评估与分析

时间:2023-06-29 理论教育 版权反馈
【摘要】:表5-7 用银钎料钎焊的低碳钢接头强度Table 5-7 The tensile strength of steel joints, brazed with silver base filler metals(续)图5-15~图5-19分别所示为国外有关的用银钎料钎焊的碳钢接头的应力-破坏性能[18]。图5-16 碳钢接头的应力-破坏性能 Fig.5-16 Stress-rupture properties of steel joints,brazed with BAg40CuZnCd图5-17 碳钢接头的应力-破坏性能 Fig.5-17 Stress-rupture properties of steel joints,brazed with BAg44CuZn图5-18 碳钢接头的应力-破坏性能 Fig.5-18 Stress-rupture properties of steel joints,brazed with BAg25CuZn图5-19 碳钢接头和1Cr18Ni9Ti不锈钢接头的应力-破坏性能 Fig.5-19 Stress-rupture properties of steel joint and stainless steel1Cr18Ni9Ti joint,brazed with BAg50CdCuZn filler metal ——碳钢——不锈钢

钎焊接头强度测试:强度评估与分析

用银钎料钎焊的低碳钢接头强度见表5-7。

表5-7 用银钎料钎焊的低碳钢接头强度Table 5-7 The tensile strength of steel joints, brazed with silver base filler metals

978-7-111-57708-9-Chapter05-27.jpg

(续)

978-7-111-57708-9-Chapter05-28.jpg

图5-15~图5-19分别所示为国外有关的用银钎料钎焊的碳钢接头的应力-破坏性能[18]

978-7-111-57708-9-Chapter05-29.jpg

图5-16 碳钢接头的应力-破坏性能(钎料BAg40CuZnCd) Fig.5-16 Stress-rupture properties of steel joints,brazed with BAg40CuZnCd(www.xing528.com)

978-7-111-57708-9-Chapter05-30.jpg

图5-17 碳钢接头的应力-破坏性能(钎料BAg44CuZn) Fig.5-17 Stress-rupture properties of steel joints,brazed with BAg44CuZn

978-7-111-57708-9-Chapter05-31.jpg

图5-18 碳钢接头的应力-破坏性能(钎料BAg25CuZn) Fig.5-18 Stress-rupture properties of steel joints,brazed with BAg25CuZn

978-7-111-57708-9-Chapter05-32.jpg

图5-19 碳钢接头和1Cr18Ni9Ti不锈钢接头的应力-破坏性能(钎料BAg50CdCuZn) Fig.5-19 Stress-rupture properties of steel joint and stainless steel1Cr18Ni9Ti joint,brazed with BAg50CdCuZn filler metal ——碳钢——不锈钢